LOCTITE® 263 is a red, dual cure, acrylic dimethacrylate ester fluorescent threadlocker designed for the permanent locking and sealing of threaded fasteners. It cures between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. It works on active metals (e.g. brass, copper) and passive substrates such as

LOCTITE® 567™ provides robust curing performance. It not only works on active metals (e.g. brass, copper) but also on passive substrates such as stainless steel and plated surfaces. The high lubricating properties of this Cure Time 125 100 75 50 25 0 0min 30min 1h 3h 6h 24h 72h 168h 40 °C 22 °C 5 °C Cure Speed vs. Activator

Cure time is a minimum of 24 hours High viscosity, thixotropic Medium strength Has a specific gravity of 1.08 Slow curing means that you have time to adjust your fittings Use for thread sizes up to M80 Suitable for use on coarse threads Seals to burst strength on most pipe systems when it is fully cured Offers a breakaway torque of 7Nm

Container Size 50 mL ; Container Type Tube ; Curing Time 72 hr ; Odor/Scent Slightly ; Series 572 

New Level1 2. Power Transmission - Belts, Chains & Couplings

Loctite 572 white thread sealant is compatible with metal materials with a 72 hr cure time. Delivers great performance with a shear strength of 70 psi and 

Cured for 1 week @ 22 °C Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m: M10 zinc phosphate steel nuts and bolts Hot Strength Tested at temperature % Strength @ 22 °C Temperature, °C 100 75 50 25 0 0 50 100 150 Heat Aging Aged at temperature indicated and tested @ 22 °C % Initial Strength @ 22 °C Exposure Time, hours

2022. 7. 14. · TDS LOCTITE® 574™, August-2005 % of Full Strength on Steel Cure Time 100 75 50 25 0 0 5min 10min 30min 1h 3h 6h 24h 72h 40 °C 22 °C 5 °C Cure Speed vs. Activator Where cure speed is unacceptably long, or large gaps are present, applying activator to the surface will improve cure speed. The graph below shows the shear strength developed

Cure Speed vs. Substrate. The rate of cure will depend on the substrate used. The graph below shows the breakaway strength developed with time on M10 steel nuts 

Description. Loctite 572 is a medium strength thread sealant suitable for coarse threads and thread sizes up to M80, this methacrylate based sealant is ideal for metal pipes and fittings. Loctite. 572 Low Strength Slow Cure Pipe Seal. 250ml.