LOCTITE AA 326 is a yellow to amber, no-mix, medium viscosity (thixotropic) structural and magnet bonder which is activated with LOCTITE SF 7649.

TDS LOCTITE® 326, May-2004 TYPICAL PERFORMANCE OF CURED MATERIAL Adhesive Properties After 24 hours @ 22 °C, Activator 7649 on 1 side (psi) (3,500) After 24 hours @ 22 °C, Activator 7649 on 2 sides Lap Shear Strength, ISO 4587: Steel (grit blasted) : 0.25 mm gap N/mm² ≥13.80LMS (psi) (2,000) TYPICAL ENVIRONMENTAL RESISTANCE Cured for

Lijmen van metalen, glas, kunststoffen, rubber, poreuze materialen, enz. In combinatie met activator 7649 Lijmen van metaal op metaal (adhesive).

Loctite 326 & 7649 Anaerobic and activator UK Approving Authority Approval Type Date of Approval WRAS Potable Water 12/31/ Registration Number Standard Approval Status 1612522 BS 6920 Expired Country Contact Certificate of Approval External Link:

Henkel Loctite 7649 MIL-SPEC Primer N decreases the set-up time of Loctite brand threadlockers and increases breakaway torque on most fastener surfaces. This anaerobic primer allows application of threadlockers in cold weather. Contains no ozone-depleting compounds. Mil Spec: Mil-S-22473E Grade N Form R. ASTM-D5363: Approved.

326 Fast Fixture Structural Acrylic Adhesive for use with 7649 Promoter, Light Amber, 50mL Bottle #135402-30769. PLEASE DO NOT HESITATE TO CONTACT THE 

Add to comparison. LOCTITE SF 7649 is a solvent-based activator for surface preparation that provides for low temperature curing. LOCTITE® SF 7649 is designed to promote the curing speed of LOCTITE anaerobic adhesives and sealants without any significant loss of joint strength. It is especially recommended for applications with passive metals

Add to comparison. LOCTITE SF 7649 is a solvent-based activator for surface preparation that provides for low temperature curing. LOCTITE® SF 7649 is designed to promote the curing

TDS LOCTITE® 326, May-2004 TYPICAL PERFORMANCE OF CURED MATERIAL Adhesive Properties After 24 hours @ 22 C, Activator 7649 on 1 side Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² ≥15.20LMS (psi) (2,200) Steel (grit

Where bond gaps are large (up to a maximum of 0.5 mm), or faster cure speed is required, Activator 7649 should be applied to both surfaces. Parts should be assembled immediately (within 1 minute). 4. Excess adhesive can be wiped away with organic solvent. 5. Bond should be held clamped until adhesive has fixtured. 6.

LOCTITE® SF 7649 depend on the adhesive used and the substrate bonded. Fixture Time, ISO 4587, seconds: Steel (degreased) using LOCTITE® 326 ,, single side activation ≤30 (Fixture time is defined as the time to develop a shear strength of 0.1 N/mm²)